Pliogrip Resins & Chemicals Pvt Ltd

PLIOGRIP P777 GENERAL PURPOSE ROOFLIGHT RESIN

PLIOGRIP P777 GENERAL PURPOSE ROOFLIGHT RESIN

 General Description

PLIOGRIP P777 is a general-purpose low viscosity, fast curing, UV stabilized general purpose rooflight resin obtain best possible Clarity, the glass mat must be clean, dry have high solubility binder. Powder bonded mats usually wet out more quickly and allow more resins to penetrate inside the glass strands. This results in superior translucency of the sheets and also to reduce the tendency to develop fiber pattern on prolonged exposure to atmosphere. Maximum Clarity depends on the state of cure of the resin and is usually obtained over a period of 24 hours at ambient temperature. PLIOGRIP P -777 are suitable for the manufacture of translucent roof sheets, domo lights, canopies and van roofs etc.

  TYPICAL PROPERTIES OF PLIOGRIP P777 IN LIQUID STAGE

 

Appearance                                      

Clear Liquid

Specific Gravity @ 25°C                

1.11 + 0.02

Viscosity @ 25°C (CPS)                 

              200 -  300

Volatile Content (Wt %)  

              40 + 2

Acid Value (mgs of KOH/gm)     

              25 + 5

 

 

 TYPICAL GEL TIME AT 25°C IS AS FOLLOWS :( 100gms resins)

 

PLIOGRIP s 1021 3% Cobalt

PLIOGRIP q 8013  50% MEKP

GEL TIME (Minutes )

                 1.0

1.0

52

                 1.5

1.5

25

                 2.0

2.0

18

                 2.5

2.5

8

 

The above gelation time decreases approx. by 30% at 30°C and increases approx. by 50% at 20°C.

 TYPICAL  PROPERTIES OF CURED UNREINFORCED RESIN

 

Tensile Strength (Kg/Cm²)                    

600 - 650

Flexural strength (Kg/Cm²)                  

900 - 1000

Heat Distortion Temperature (°C)      

78

Barcol Hardness                                      

40

Elongation at break(%)                         

1.5

 


 (The specimens for testing are cured for 24 hours at Room temperature followed by Post Curing for 4 hours at 80°C)
 POST CURING REQUIREMENTS:

Satisfactory laminates for many applications can be made by curing the laminate at ambient temperatures. However for achieving optimum properties the laminate should be post cured for a period of 4 hours at 80°C. The post curing is most effective when carried out immediately after the 24 hours ambient temperature cure.

Storage & Handling :

Should be stored in closed containers in cool conditions away from direct Sunlight. Resins exposed to direct Sunlight may lead to premature gelation even in the absence of a Catalyst.   Shelf life of Resin @ 25°C. about 6 months from the date of manufacturing.

Most of our resin contain styrene monomer and are classified as highly flammable liquids. Working areas should be well ventilated since styrene has a threshold value of 1000ppm in normal working atmosphere  .It is also an eye skin irritant. Hence, Goggles and gloves are recommended while handling our Resins

  Caution:

Pliogrip Q 8013 MEKP should never be mixed with Pliogrip S 1021 Cobalt, as this would cause explosion. The Pliogrip S 1021 Cobalt should be blended into the resin first. The Pliogrip Q 8013 MEKP should be added just before use.


 NOTE :

The above information given for general guidance for the use of our Product, keeping in view the variable operating/process conditions and methods, it is recommended that each consumer evaluates the suitability of the products. The company does not accept any responsibility whatsoever for any damage, injury or loss resulting from the use of above information.


 METHOD OF TEST : THE METHOD OF TEST AND TOLERANCES ARE AS PRESCRIBED IN BS: 3532: 1962, BS:2782 : 1957 AND IS 6746 : 1972.